Organic mesh template-based laminated object manufacturing to fabricate ceramics with regular micron scaled pore structures

A new aqueous slurry-based laminated object manufacturing process for porous ceramics is proposed: firstly, an organic mesh sheet is pre-paved as a pore-forming template before slurry layer scraping; secondly, the 2D pattern is built with laser outline cutting of the dried mesh–ceramic composite layer; finally, the pore structure is formed after degreasing and sintering. Alumina parts with porosities of 51.5 %, round hole diameters of 80 ± 5 μm were fabricated using 70 wt. % solid content slurry and 100 mesh nylon net. Using an organic mesh as the framework and template not only reduces the risk of damage of the green body but also ensures the regularity, uniformity and connectivity of the micron scaled pore network. The layer-by-layer drying method avoids the delamination phenomenon and improves the paving density. The new method can realize the flexible design of the pore structure by using various organic mesh templates.     

窑头袋收尘器滤袋异常磨损的原因及处理办法

我公司1#生产线的窑头使用布袋收尘器，型号：HMMC391-4×4，处理风量：1 350 000 m3/h，过滤风速<0.9 m/min，收尘器风室4 排×4 列。投入使用3个月后停机检查，发现第一排4 个风室的滤袋较多底部被磨穿，主要集中在灰斗四周的前3 环区域，前两排风室其他位置的滤袋也较多出现异常磨损，但后 两排风室的滤袋却完好无损。     

深共融溶剂催化制备二酯类化合物

二酯类化合物广泛应用于有机中间体、药物、增塑剂、香料等领域,开发其绿色、高效的合成新方法具有重要意义.报道了以二元羧酸(或二羧酸酐)和脂肪醇为原料,以深共融溶剂(DESs)为催化剂催化合成二酯类化合物.以n(氯化胆碱):n(对甲苯磺酸)=1:2为催化剂,产率最高可达95％,并且DESs使用8次后产率仍保持在88％以上.运用1HNMR和13CNMR对产物进行了结构表征.该方法具有操作简单、产率高、易分离和催化剂可循环使用等优点.     

微纳层叠聚丙烯腈凝胶流动特性的数值模拟研究

建立了层叠流道的三维模型和有限元网格模型，根据流变测试数据，采用Polymat对物料的黏度模型参数进行拟合，并利用Polyflow软件对聚丙烯腈（PAN）凝胶在层叠流道内的三维等温流动过程进行了数值模拟分析。研究发现，当入口流量增大时，层叠流道出口速度的不均匀性增加；沿流动方向流道内压力逐渐降低，并在出口处降低至同一最低值；流道进出口压力差与入口流量大小具有正相关性；在流道的中心截面上剪切速率分布均匀，波动较小。     

气相色谱法测定焦油中微量苯稠杂环化合物

利用蒸馏分离—气相色谱法技术,建立了同时测定煤焦油中苊、氧芴和芴的分析方法。通过对色谱条件的优化,以甲苯为溶剂,正十二烷为内标物,将煤焦油馏分采用DB-5毛细管柱,对煤焦油中苊、氧芴和芴定量分析。分析结果表明:3种主要成分线性关系良好,相关系数均大于0.9995,加标回收率为95.4%~102.4%,相对标准偏差为2.89%~7.14%。该方法分离效果好,检测结果准确、可靠。     

车门铰链系统与车门下沉刚度的相关性

针对某型车门下沉问题,通过台架试验获得车门、铰链和车身等各单因素下沉量和车门绞链系统整体下沉量,对单因素下沉量与系统整体下沉刚度进行线性拟合分析,得到车门铰链系统各单因素与系统下沉刚度的相关度排序.对前、后车门分别选取相关度较高的单因素进行优化,最终改进方案的仿真和试验结果证明该方案可有效地提升车门下沉刚度.采用定量分析法可快速找出影响下沉刚度的敏感因素,并能够快速生成优化方案,为新车型设计提供参考.     

基于MATLAB灰色Elman网络中长期电力负荷预测

良好的负荷预测模型能够精准且快速地计算预测值,有利于合理地规划分配电能,提升电网运行稳定性.基于MATLAB搭建灰色Elman网络电力负荷预测模型,参考安徽省淮南市"十三五"能源规划[1],以对淮南市进行中长期电力负荷预测为例,同时设置基于MATLAB搭建的Elman网络和灰色理论中的GM(1,1)模型为对照组进行对比仿真实验.提出灰色Elman网络相比对照组具有更高的运算精度,灰色Elman网络对比Elman网络有更好的训练效果.     

八段锦在女大学生篮球教学后疲劳恢复中的应用

运用八段锦进行女大学生篮球教学后疲劳恢复,并与传统恢复手段拉伸运动进行比较实验,探索快速消除运动性疲劳的方法.研究结果显示:女大学生运用八段锦进行篮球教学后的疲劳恢复,其心率恢复明显的优于传统拉伸运动;学生的主观感觉疲劳恢复程度也明显的优于传统拉伸运动.结果表明,八段锦能够有效促进女大学生生理和心理疲劳的恢复.     

电石汽车卸料、破碎、除尘、输送一体化智能系统——中吴天玺系统

针对PVC企业电石车间存在的粉尘污染严重、人工操作安全隐患大等问题,江苏中吴环境工程设计研究有限公司开发了电石汽车卸料、破碎、除尘、输送一体化智能系统(即中吴天玺系统),对该系统的工艺流程、系统组成、占地空间、经济效益和社会效益簣方面进行了介绍。     

Electrodeposition of B,Ni co-doped diamond-like carbon films on AZ91D magnesium alloy: Corrosion and wear resistance

Diamond-like carbon (DLC) possesses brilliant and excellent properties, including excellent corrosion resistance as well as outstanding wear resistance. Ni and B co-doped DLC films were deposited on AZ91D magnesium alloy by electrodeposition under mild conditions (300 V and 25°C). Uniform and dense morphology of co-doped DLC films were observed, and Ni and B were uniformly incorporated into the carbon-based films. Among all the electrodeposits, the appearance of D and G peaks near 1330 and 1570 cm⁻¹ revealed that the as-deposited films were typical DLC films. As the addition of Ni was increased to 0.05 g, the highest microindentation hardness, the lowest friction coefficient, and wear loss were achieved to be 164.5 HV, 0.3, and 0.6 × 10⁻⁵ kg/m, respectively. The amorphous carbon films fabricated at 0.05 g Ni had the lowest corrosion current density and the most positive corrosion potential, which was mainly due to the small and dense granular structure effectively hindering the penetration of corrosion media.